GB 3087 standard seamless boiler alloy steel pipe Low pressure Medium pressure

Krótki opis:

GB T3087-2008

Super ogrzewany przewód parowy wysokiej jakości rur stalowych bez szwu węgiel niskie ciśnienie średnie ciśnienie w kotle rura

Mainly for India market with IBR certification


  • Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight
  • Min.Order Quantity: 1 PC
  • Supply Ability: Annual 20000 Tons Inventory of Steel Pipe
  • Lead Time: 7-14 days if in stock, 30-45 days to produce
  • Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.
  • Szczegóły produktu

    FAQ

    Tagi produktów

    Przegląd

    Standard: PL / T3087-2008

    Grupa gatunek: 10 #, 20 #

    Grubość: 1 - 100 mm

    Średnica zewnętrzna (okrągłe): 10 - 1000 mm

    Długość: Stała długość lub długość losowo

    Sekcja Kształt: okrągły

    Miejsce pochodzenia: Chiny

    Certyfikat: ISO9001: 2008

     

    Stop czy nie: bez szwu ze stali węglowej

    Zastosowanie: Rury kotłowe

    Obróbka powierzchniowa: Jak wymagań klienta

    Technika: walcowane na gorąco / zimno

    Obróbka cieplna: Normalizacja

    Specjalne rury: Grube ścianki rury

    Zastosowanie: Budownictwo, Fluid Transport, kocioł i wymiennik ciepła

    Test: ET / UT

    Podanie

    It is mainly used to make high-quality carbon structural steel, low pressure medium pressure boiler pipe, super heated steam seamless carbon steel pipe

    Główna klasa

    Gatunek wysokiej jakości stali węglowej konstrukcyjnej: 10 #, 20 #

     

    Składnik chemiczny

    Standard Stopień Skład chemiczny (%)
    do Si Mn P S cr Cu Ni
    GB3087 10 0,07 ~ 0,13 0,17 ~ 0,37 0,38 ~ 0,65 ≤0.030 ≤0.030 0,3 ~ 0,65 ≤0.25 ≤0.30
    20 0,17 ~ 0,23 0,17 ~ 0,37 0,38 ~ 0,65 ≤0.030 ≤0.030 0,3 ~ 0,65 ≤0.25 ≤0.30

    Właściwości mechaniczne

    Standard Stalowa rura grubość ściany Wytrzymałość na rozciąganie Granica plastyczności Wydłużenie
    GB3087 (Mm) (MPa) (MPa) %
    10 / 335 ~ 475 195 24
    20 <15 410 ~ 550 245 20
    ≥15 225

    Tolerance

    Permissible deviation of outer diameter of steel tubes

    Type of steel tube  Permissible deviation
    Hot rolled (extruded, expanded) steel tube ± 1.0% D or ± 0.50, take the greater number
    Cold drawn (rolled) steel tube ± 1.0% D or ± 0.30, take the greater number

    Permissible deviation of the wall thickness of hot rolled (extrusion, expansion) steel tubes

    Unit: mm

    Type of steel tube Outer diameter of steel tube S / D  Permissible deviation
    hot rolled (extruded) steel tube ≤ 102  – ± 12.5 % S or ± 0.40, take the greater number
    > 102 ≤ 0.05 ± 15% S or ± 0.40, take the greater number
    > 0.05 ~ 0.10  ± 12.5% S or ± 0.40, take the greater number
    > 0.10 + 12.5% S
    - 10% S
    hot expand steel tube + 15% S

    Permissible deviation of the wall thickness of cold drawn (rolled) steel tubes

    Unit: mm

    Type of steel tube grubość ściany Permissible deviation
    Cold drawn (rolled) steel tube ≤ 3 15 - 10 % S or ± 0.15, take the greater number
    > 3 + 12.5% S
    - 10% S

    Wymaganie Test

    Flattening test

    Steel tubes with an outer diameter greater than 22 mm and up to 400 mm, and wall thickness greater than 10 mm should undergo the flattening test. After the samples are flattened

    Bending test

    Steel tubes with an outer diameter not greater than 22 mm should undergo the bending test. The bending angle is 90o . The bending radius is 6 times the outer diameter of the steel tube.After bending the sample, no fissures or cracks are permitted to appear on the sample.

    Macroscopic examination

    For steel tubes directly made by continuously cast billets or steel ingots, the supplying party should guarantee that there are no white spots, impurities, sub-surface air bubbles, skull patches or layering on the cross-sectional acid pickled macroscopic tissue of the billet or steel tube.

    Non-destructive inspection

    According to the demanding party’s request, which is then negotiated between the supplying and demanding parties and indicated in the agreement, ultrasonic flaw detection may be individually performed for steel tubes. The longitudinal manual defect of the reference sample tube should meet the requirements for post-inspection acceptance grade C8 specified in GB/T 5777-1996.

     